For turning small parts | UC1 and Y axis holder + High-pressure coolant
Diamond-coated carbide: UC1 with excellent wear resistance & welding resistance is recommended because tooling tends to wear and the machined surface deteriorates due to welding, resulting in short tool life.
A good machined surface can be obtained by applying the appropriate cutting condition (low cutting depth/low feed) which reduces the chip thickness.
| ISO | Work material | Coolant | Grade | vc (m/min) (SFM) | ap (mm) (inch) | f (mm/rev) (IPR) |
|---|---|---|---|---|---|---|
 |
Tough pitch copper C1100 Rough-Finish Turning |
WET | UC1 | 50 – 150 160 – 500 | 0.02 – 0.05 .0008 – .002 | 0.2 – 2.0 .008 – .080 |
| ISO | Work material | Coolant | Grade | vc (m/min) (SFM) | ap (mm) (inch) | f (mm/rev) (IPR) |
|---|---|---|---|---|---|---|
|
Oxygen-free copper C1020 Rough-Finish Turning |
WET | UC1 | 50 – 150 160 – 500 | 0.5 – 3.0 .020 – .120 | 0.02 – 0.20 .0008 – .008 |
| TM4 |
| ISO | Work material | Coolant | Grade | vc (m/min) (SFM) | ap (mm) (inch) | f (mm/rev) (IPR) |
|---|---|---|---|---|---|---|
|
C1100 Finish Turning |
WET | UC1 | 50 – 150 160 – 500 | 0.02 – 0.05 .0008 – .002 | 0.1 – 0.5 .004 – .020 |
| TM4 | ||||||
| C1020 Finish Turning |
WET | UC1 | 50 – 150 160 – 500 | 0.02 – 0.05 .0008 – .002 | 0.1 – 0.5 .004 – .020 | |
| TM4 |
If you want longer tool life than PVD Carbide: TM4, use Diamond-Coated Carbide: UC1.
| Battery connector | |
|---|---|
|
C1100 ⌀10-20 ⌀.394 -.787 in. |
|
55 – 110 180 – 360 |
|
0.03 .0012 |
|
0.2 .008 |
|
WET |
| UC1 DCMT11T302 DCMT32.508 FNAM3 |
1000 pcs / corner
|
| PVD super coat DCGT11T302 DCMT32.508 molded chipbreaker | 50 pcs / corner |
| Electrode part | |
|---|---|
|
C1100 ⌀12 ⌀.472 in. |
|
80 262 |
|
0.05 .002 |
|
1.0 .040 |
|
WET |
| UC1 DCMT11T301 DCMT32.504 FNAM3 |
2000 pcs / corner
|
| PVD super coat DCGT11T301 DCMT32.504 molded chipbreaker | 100 pcs / corner |
For more information about this product, visit our online e-catalog, or download the catalog/product report